MUSCOVITE MICA PAPER |
Products Infomation:
Muscoivte mica paper is made by thermal chemical treatment or hydraulic separtion process using the best quality of muscovite scrap,which is first reduced to pulpand then made into the products.According to its different manufacturing process,our mica paper items like :MPM1(501),MPM2(501-2),MPM3(505),MPM3-L(506),507,511 and MPP4(P506)
| ITEM |
MPM1（501） |
MPM3-b（505） |
Basic Weight g/m2 |
82 |
130 |
160 |
80 |
165 |
300 |
AVE Deviation% |
±4 |
±4 |
±4 |
±5 |
±5 |
±5 |
Individual Deviation% |
±6 |
±6 |
±6 |
±6 |
±6 |
±6 |
Thickness mm |
0.055 |
0.035 |
0.105 |
0.055 |
0.11 |
0.20 |
Penetration S |
110 |
140 |
160 |
10 |
30 |
90 |
Conductive of the exact aqueours μS/cm |
20 |
20 |
20 |
10 |
10 |
10 |
Dielectric Strength MV/m |
25 |
25 |
25 |
14 |
14 |
14 |
Heating loss?% |
0.5 |
0.5 |
0.5 |
0.4 |
0.4 |
0.4 |
Tensile strength (N/cm) |
9.8 |
11 |
11 |
8.4 |
12.5 |
14.0 |
ITEM |
MPM3-L2（501） |
MPM3-L2（507） |
Basic Weight g/m2 |
80 |
100 |
160 |
400 |
80 |
120 |
160 |
AVE Deviation% |
±4 |
±5 |
±5 |
±5 |
±4 |
±4 |
±4 |
Individual Deviation% |
±4 |
±6 |
±8 |
±10 |
±5 |
±5 |
±6 |
Thickness mm |
0.055 |
0.065 |
0.10 |
0.25 |
0.052 |
0.075 |
0.10 |
Penetration S |
15 |
20 |
35 |
115 |
8 |
12 |
17 |
Conductive of the exact aqueours μS/cm |
9 |
9 |
9 |
9 |
9 |
9 |
9 |
Dielectric Strength MV/m |
14 |
14 |
15 |
15 |
14 |
15 |
16 |
Heating loss % |
0.4 |
0.4 |
0.4 |
0.4 |
0.3 |
0.3 |
0.3 |
Tensile strength (N/cm) |
4.2 |
3.0 |
3.6 |
7.5 |
2.0 |
3.0 |
3.5 |
|
| |
|
|
Phlogopite mica paper |
Products Infomation:
Phlogopite mica paper is made by thermal chemical treatment or hydraulic separation process usind the best quality of phlogopite mica paper which is cutted and make into roll paper.It is a kind of? high insulating material and can be widly used in different electric heater and home appliances
| ITEM |
MPP4(P506) |
Basic Weight g/m2 |
80 |
100 |
150 |
350 |
AVE Deviation% |
±5 |
±5 |
±5 |
±5 |
Individual Deviation% |
±4 |
±4 |
±7 |
±8 |
Thickness mm |
0.050 |
0.065 |
0.095 |
0.22 |
Penetration S |
8 |
15 |
45 |
130 |
Conductive of the exact aqueours μS/cm |
10 |
10 |
10 |
10 |
Dielectric Strength MV/m |
10 |
11 |
12 |
11 |
Heating loss % |
0.4 |
0.4 |
0.4 |
0.4 |
Tensile strength (N/cm) |
2.5 |
2.8 |
3.6 |
6.0 |
|
| |
|
SPECIAL MICA PAPER |
Products Infomation:
1.506-D Mica paper was produced by hydraulic separation process using the best mica scrap material from Chinese DANBA mica mines.This uncalcined mica paper? has very good dielectric strength and can be widly used in making middle-glue,less-glue mica tape for generator .We can produced? basic weight from 70-140g/m2/
2.506-A Mica paper can be used in making mica tape which has special require of? light weight and thin,such as for generator (Wind energy),electromagnetic mica tape etc. |
| |
|
GENERATOR MICA TAPE |
Products Infomation:
Generator mica tape was produced by non-alkaline glass cloth,with good quality mica paper and epoxy resin.In the nomal temperature,it is flexible .It can be used in generator and motor.
Generator mica tape ( good electric strength,porosity),with solvent-free immersion paint,cab work well for F grade high voltage generator when using VPI .
| ITEM |
UNIT |
MICA TAPE
SM-0561 |
Appreance |
/ |
Adhensive uniformity;no adhension;no powder; |
Disc Diameter |
mm |
95±5 115±5 |
Width |
mm |
15±1 20±1 25±2 30±3 35±3 |
Thickness |
mm |
0.14±0.02 |
Weight |
g/m2 |
196±15 |
Mica paper |
％ |
≥80 |
Adhensive |
％ |
5±1 |
Glass cloth |
g/m2 |
20±2 |
Strength |
N/cm |
≥80 |
Stiffness |
N/m |
≤60 |
Porosity |
s/100ml |
≤800 |
Electric strength |
MV/m |
≥10 |
Gel time |
min/ 170℃ |
As required |
Storage time |
/ |
20c 12month |
|
| |
|
MICA POWDER |
| |
|
PHP5 RIGID PHLOGOPITE MICA PLATE |
Products Infomation:
Item:PHP5
PHP5 rigid phlogopite mica plate was produced by good quality phlogopite mica paper and organic silicon resin by baking and pressing process.
Usage:PHP5 has good thickness uniformity,electric property,mechnical property.The working temperature is 850C.It is a new insulating material which can be used many electric applicance,such as industry electic cooker,printer,microwave evon,water heater.
Item |
Rigid phlogopite mica plate PHP5 |
Mica paper |
Phlogopite mica paper |
Adhensive |
Organic-silicon resin |
Mica content |
≥ 90% |
Glue content |
≤ 10% |
Thickness |
0.10 ～ 2.0 |
Thickness Error(mm) |
Average |
±0.02 － ±0.05 |
Points |
±0.05 － ±0.08 |
Density |
1.6-2.2 |
Heating lossing % |
≤0.60 |
Curving strength |
≥16 |
Broken voltage |
>18 |
Resistance |
100 － 600 |
Working termperature |
850℃ |
Standard size |
1000 × 600 1000 × 1200 |
Test standard |
GB5019 － 85, IEC371 |
★Thickness<0.2mm,the broken voltage should be decided again. |
| |
|
HP5-1 muscovite flexible mica plate |
Products Information:
HP5-1 Muscovite mica plate is produced by special organic-silicon resin with mica paper by baking and pressing.
Usage:HP5-1 muscovite mica plate has good character of flexible,working temperature 550C;Phlogopite mica paper working temperature is 850C.It can be made into roll( diameter 10mm).It is a new insulating material used in hair dryer,microwave oven,electric iron etc.
| Item |
Muscovite flexible mica plate HP5-1 |
Mica paper |
Muscovite paper |
Adhensive |
Organic-silicon resin |
Mica content |
≥ 90% |
Glue content |
≤ 10% |
Thickness |
0.10 ～ 2.0 |
Thickness Error(mm) |
Average |
±0.02 － ±0.25 |
Points |
±0.04 － ±0.06 |
Density |
1.6-2.2 |
Heating lossing % |
≤2.00 |
Curving strength |
/ |
Broken voltage |
>15 |
Resistance |
/ |
Working termperature |
550℃ |
Standard size |
1000 × 600 1000 × 1200 |
Test standard |
GB5019 － 85, IEC371 |
★Thickness<0.2mm,the broken voltage should be decided again. |
| |
|
|
|
|